Showing items 1 - 15 of 16.

Add to Quick Collection   All 16 Results

Sort:
 Add All Items to Quick Collection
Date: 2018/10/02
Language: en
Type: Text
Identifier: tut:5502
Description: This article outlines the behaviour of water-soluble chitosan as an effective inhibitor on aluminium alloy in 3.65% NaCl at room temperature. The inhibitive ability of water-soluble chitosan was exami ... More
Full Text: Full Text
Date: 2018/07/23
Language: en
Type: Text
Identifier: tut:5319
Description: Corrosion processes are responsible for huge losses in industry. This deterioration of components results in loss of plant efficiency, total shutdown and aggressive damage in a number of industries. T ... More
Full Text: Full Text
Date: 2018/02/08
Language: en
Type: Text
Identifier: tut:5297
Description: Corrosion of metal is a costly material science problem which originates from the day of metal discovery. Corrosion inhibitor usage is an effective way of addressing metallic corrosion in aggressive e ... More
Full Text: Full Text
Date: 2017/06/05
Language: en
Type: Text
Identifier: tut:6532
Description: The synergistic effects of monoethylene glycol (MEG) and leaf extract of Sida acuta on UNS S30403 stainless steel under sand deposit in aerated 3.5-wt.% NaCl solution were studied through open circuit ... More
Full Text: Full Text
Date: 2017/01/01
Language: en
Type: Text
Identifier: tut:5991
Description: Corrosion processes are responsible for huge losses in industry. Though organic, inorganic and mixed material inhibitors were used for a long time to combat corrosion, the environmental toxicity of or ... More
Full Text: Full Text
Date: 2016
Language: en
Type: Text
Identifier: tut:5113
Description: The effect of allium cepa extract as an inhibitor on mild steel corrosion in 0.5M H2SO4 was investigated at ambient temperature. The experiments were performed with gravimetric and potentiostatic pola ... More
Full Text: Full Text
Date: 2016
Language: en
Type: Text
Identifier: tut:5111
Description: A study of the effect of allium cepa extract as an inhibitor on mild steel corrosion in 0.5M HCl was made at ambient temperature. The experiments were performed with the weight loss/corrosion rate and ... More
Full Text: Full Text
Date: 2016
Language: en
Type: Text
Identifier: tut:5109
Description: The corrosion inhibition effect of allium sativum(garlic) extract as a ‘green’ inhibitor on α-brass in 0.5M HNO3 was studied at ambient temperature. Weight loss and corrosion rate and potentiodynamic ... More
Full Text: Full Text
Date: 2016
Language: en
Type: Text
Identifier: tut:5114
Description: The inhibition effect of zinc oxide on the corrosion behaviour of embedded mild steel rebar in concrete has been investigated by potential measurement, such as pH and gravimetric (weight loss) methods ... More
Full Text: Full Text
Date: 2015
Language: en
Type: Text
Identifier: tut:4800
Description: The corrosion resistance behaviour of 12Cr martensitic stainless steel was evaluated in different concentrations of H3PO4 and H3PO4 + NaCl. Corrosion inhibition of the tested samples in 1M H3PO4 was a ... More
Full Text: Full Text
Date: 2015
Language: en
Type: Text
Identifier: tut:4798
Description: The electrochemical behaviour of 2-dimethylaminoethanol (DMA) on the corrosion of Type 304 austenitic stainless steel in dilute hydrochloric solution was investigated through a weight-loss technique, ... More
Full Text: Full Text
Date: 2013/06/06
Language: en
Type: Text
Identifier: tut:5633
Description: The inhibition effect of Vernonia amygdalina (bitter leaf) extract on the corrosion behaviour of embedded mild steel rebar in concrete has been investigated by electrochemical potential measurement, p ... More
Full Text: Full Text
Date: 2011/09/18
Language: en
Type: Text
Identifier: tut:5635
Description: The effect of C. Papaya (pawpaw) leaves and C. Sinensis (tea) extracts as an organic „green‟ inhibitor on the corrosion of α β (duplex) brass (65-35% Cu-Zn alloy) in 1MHNO3 (nitric acid) was studied a ... More
Full Text: Full Text
Date: 2011/08/04
Language: en
Type: Text
Identifier: tut:5634
Description: Corrosion and plants extracts inhibitive protection of mild steel specimens immersed in 0.5 M hydrochloric acid was investigated at ambient temperature by gravimetric and metallographic methods. Extra ... More
Full Text: Full Text
Date: 2011/07/05
Language: en
Type: Text
Identifier: tut:5647
Description: The corrosion and protection of a mild steel reinforcement in concrete, partially immersed in 5% sodium chloride solution, was investigated at ambient temperature by potential monitoring technique. Th ... More
Full Text: Full Text